Free Content Selective synthesis of conjugated enynes from α-arylalkynols using LiCl-Acidic Al2O3 under solvent-free conditions  

7H-benzimidazo[2,1-a]benz[de]isoquinolin-7-one compounds were prepared in a selective manner by reaction between o-phenylenediamines and appropriate 1,8-naphthalenedicarboxylic anhydrides using acidic alumina under microwave irradiation  

γ-Alumina is used to catalyze the Cannizzaro reaction in the absence of any base under microwave irradiation in high yields. In the case of terephthalaldehyde the reaction is carried out with high selectivity  

CdS nanocrystals were thermochemically (thermally activated) synthesized thorough the reaction between CdSO4 and Na2S 2O3 in an aqueous solution. Thioglycolic Acid (TGA) was used as the capping agent and catalyst of the reaction. The method was based on heat activated dissociation of Na2S2O3 and controllable release of S and free electrons in the solution. CdS NCs were formed by heating the sample solution at 96 C for 1 h. The results of optical spectroscopy and transmission electron microscopy demonstrated round shape NCs with sizes about 3.0 nm. The nanocrystals were also luminescent and represented a broad emission with a peak located at 515 nm and FWHM of 160 nm. Several samples were... 

Conjugated enynes, dienes and simple olefins have been cleanly and selectively synthesized, good-to-excellent yields, by dehydration of corresponding alcohols using focused microwave irradiation on the surface of LiCI-acidic alumina  

We report a novel method of growing red luminescent (635 nm) Mn-doped CdS (CdS:Mn) nanoparticles capped by an inorganic shell of Mn(OH)2. CdSO4, Na2S2O3 and Mn(NO3)2 were used as the precursors, and thioglycerol (C3H8O2S) was employed as the capping agent and also the catalyst of the reaction. Using these materials resulted in very slow rate of the reaction and particles growth. The self-assembled one-pot process was performed at pH of 8 and Mn:Cd ratio of 10, and took about 10 days for completion. CdS:Mn nanoparticles are slowly formed in the first day of the process; however, the luminescence is weak. After 7 days, the solution turns white turbid through the formation of additional... 

In this work, we propose a combined photochemical-chemical method that enables us to grow CdS nanoparticles with ångström precision. CdS nanoparticles were formed through a photo-induced reaction between CdSO 4 and Na2S2O3. Thioglycerol (C 3H8O2S) was used as the capping agent. Fine tuning of the size was subsequently carried out by controlling the pH of the solution. Optical absorption spectroscopy was mainly used to monitor the process of particle formation, and to measure the bandgap and size. X-ray diffraction spectra confirmed the optical sizes and demonstrated crystalline nanoparticles. In the presence of the capping agent there was a dark growth that was completely dependent on the pH... 

The optical and electrical properties of semiconductor nanoparticles are strongly dependent on their size. A flexible control of the size of the nanoparticles is of interest for tuning their properties for different applications. Here we use a coupled method to control the size of CdS nanoparticles. The method involves the photochemical growth of CdS nanoparticles together with the use of a capping agent as an inhibiting factor. CdS nanoparticles were formed through a photoinduced reaction of CdSO4 and Na2S2O3 in an aqueous solution. Mercaptoethanol (C2H6OS) was used as the capping agent, and we investigated the effect of illumination time, illumination intensity and the concentration of... 

A novel superabsorbent hydrogel composite based on gelatin has been prepared by graft copolymerisation of acrylic acid and acrylamide in the presence of kaolin powder, using methylene-bisacrylamide (MBA) as a crosslinking agent and ammonium persulfate as an initiator. The synthetic variables affecting the water absorbency of the resulting superabsorbent composite were studied and the composite structure was confirmed using FT-IR spectroscopy. A new absorption band at 1728 cm-1 in the composite spectrum confirmed the presence of a kaolin-organic polymer linkage. The effect of kaolin content and MBA concentration showed that increasing these parameters decreased the water absorbency of the... 

Arylalkynols were converted into both conjugated enynes and arylacetylenic compounds using p-TsCl/Al2O3 and KOH/Al2O3 respectively in classical heating or microwave irradiation methods in good yields  

TiO 2 nanorods, TiO 2 nanorod/TiO 2 nanoparticle and TiO 2 nanorod/ZnO nanoparticle composite structures were integrated as photoanodes in backside illuminated dye-sensitized solar cells (DSSCs). Incorporation of TiO 2 nanoparticles into the bare nanorods increased the dye loading and improved the short-circuit current density (J sc) from 2.22 mA/cm 2 to 3.57 mA/cm 2. ZnO nanoparticles electrochemically grown into the TiO 2 nanorod layer could increase the surface area. Nevertheless, this considerably reduced the J sc to 0.57 mA/cm 2 and consequently cell efficiency. Electrochemical impedance spectroscopy (EIS) results showed that ZnO incorporated samples have better effective diffusion... 

We report a new method of growing Mn-doped CdS (CdS:Mn) nanoparticles in an aqueous solution at boiling temperature. The idea is to use precursors that react only at high temperature, in order to gain crystalline luminescent nanoparticles. CdSO4, Mn(NO3)2 and Na 2S2O3 were used as the precursors, and thioglycerol was employed as the capping agent and also the reaction catalyst. Na2S2O3 is thermally sensitive and it releases S2- ions upon heating. The CdS:Mn nanoparticles obtained are about 4 nm in size and show both cubic and hexagonal crystalline phases with a ratio of 35% to 65%. The luminescence of nanoparticles contains a peak at 580 nm, which is related to Mn2+ ions. Prolonged reaction... 

CdS nanocrystals were prepared through a thermally activated (thermochemical) method. The synthesis was performed in two different oxygen-saturated and Ar purged atmospheres. Na2S2O3 was used as a heat-sensitive source of S in the experiments. Thioglycerol was also applied as the capping agent to restrain the growth. The growth was activated by heating and controlled by solution pH. The results demonstrated a considerably higher luminescence intensity for the synthesis in oxygen-saturated atmosphere. This could show the role of luminescent oxygen trap states created inside the CdS nanocrystals. The improved luminescence was observed for the synthesis at different solution pHs. Nevertheless,... 

CdS nanoparticles were grown using CdSO4 and Na 2S2O3 as the precursors and thioglycerol (TG) as the capping agent. TG was shown to exhibit a catalytic role in the reaction and also acted as a capping agent. It was demonstrated that size growth is linearly related to the temperature of the reaction, i.e.the sizes can be controllably adjusted by temperature. The crystalline phase of the nanocrystals was also dependent on the temperature of growth: higher temperature favours the cubic phase. The pH also plays an important role in nanoparticle growth, as lower pH leads to a higher release rate of sulfur species. At pH as high as 10, the growth rate remains slow even at boiling temperature. This... 

Purpose: This study aims to use big data analysis and sheds light on key hotel features that play a role in the revisit intention of customers. In addition, this study endeavors to highlight hotel features for different customer segments. Design/methodology/approach: This study uses a machine learning method and analyzes around 100,000 reviews of customers of 100 selected hotels around the world where they had indicated on Trip Advisor their intention to return to a particular hotel. The important features of the hotels are then extracted in terms of the 7Ps of the marketing mix. This study has then segmented customers intending to revisit hotels, based on the similarities in their reviews.... 

Microwave induced Cannizzaro reaction, which was performed in presence of neutral γ-alumina as a polymeric catalyst, was discussed. Cannizzaro reaction was carried out on alumina surface and other unknown products were also obtained. Solvent extraction method was utilized to isolate mild and selective benzyl alcohol and carboxylic acids  

This article describes the synthesis and swelling behavior of a superabsorbing hydrogel based on sodium alginate (NaAlg) and polyacrylonitrile (PAN). The physical mixture of NaAlg and PAN was hydrolyzed with a solution of NaOH to yield an alginate-poly(sodium acrylate-co-acrylamide) [Alg-poly(NaAA-co-AAm)] superabsorbent hydrogel. A proposed mechanism for hydrogel formation was suggested, and the structure of the product was established with Fourier transform infrared spectroscopy. The effects of reaction variables were systematically optimized to achieve a hydrogel with a swelling capacity as high as possible. Under the optimized conditions concluded, the maximum capacity of swelling in... 

In this work we report a fast two-step microwave activated synthesis of the ZnS:Mn nanocrystals. Zn(NO3)2 and Na2S 2O3 were used as the precursors and Mn(NO 3)2 was employed as the source of the impurity. The aqueous synthesis was based on the heat sensitivity of Na2S 2O3, which releases some S species on heating. Consequently, the reaction was well activated under microwave irradiation resulting in formation of ZnS:Mn nanocrystals. Thioglycerol (TG) was also used as the capping agent and the catalyst of the reaction. The synthesis process was done in two steps, i.e. 1 min irradiation without TG and then injection of TG and continuation of irradiation. ZnS:Mn nanocrystals were quickly formed... 

CdS nanoparticles were synthesized by a thermochemical method by using Na2S2O3 and CdSO4 as the precursors and thioglycerol as the capping agent. We have investigated the effect of different temperatures on the size and crystalline phase of the CdS nanoparticles. The results of the optical spectroscopy and XRD analyses clarified that increasing the synthesis temperature increased the final nanoparticles size and also changed the crystalline phase of the particles from hexagonal to cubic phase. The size of the synthesized particles was less than 4nm. TEOS was also used in cooperation with thioglycerol for better surface passivation. The results of the PL analysis showed that using this... 

We have synthesized CdS NCs (NCs) by a thermochemical approach. CdSO 4 and Na2S2O3 were used as the precursors and thioglycolic acid (TGA) was used as capping agent molecule. The structure and optical property of the NCs were characterized by means of XRD, TEM, UV-visible optical spectroscopy and photoluminescence (PL). XRD and TEM analyses demonstrated hexagonal phase CdS NCs with an average size of around 2 nm. Synthesized NCs exhibited a band gap of about 3.21 eV and showed a broad band emission from 400 to 750 nm centered at 503 nm. This broad band emission is related to surface states of CdS and our results showed that the emission peak can be attributed to the interstitial sulfur. The...