Sharif Digital Repository

The effect of heat treatment on the axial crushing behavior of thin-walled aluminum 6061 alloy tubes is studied in this work. For this purpose, thin-walled grooved specimens were subjected to different aging heat treatments to obtain different work hardening behaviors. Afterward, quasi-static axial compression tests were achieved to evaluate the crushing behavior. Additionally, a finite element method simulation was employed to determine the distributions of stress, strain, and imposed damage during axial compression. Results show that the optimum energy absorption characteristics can be obtained using moderated strain hardening exponent, ''n''. Low strain hardening exponent results in the... 

The effects of die geometry on the deformation behavior of aluminum 6061 alloy tube in a novel severe plastic deformation (SPD) process called tube channel pressing (TCP) were studied using the Abaqus 6.10 software. Using the optimized die geometry, 1 to 3 passes of TCP is imposed not only to validate the simulation results, but also to investigate the performance of TCP as a SPD process. The finite element method (FEM) simulation results show that the moderated plastic strain, the lower inhomogeneity in distribution of plastic strain, and the lower risk of fracture during process can be obtained using the proper die geometry. In addition, the imposed strain is a mixture of shear strain and... 

The deformation behavior of solid solution-treated AA6061 tubes in a novel severe plastic deformation process named Tube Channel Pressing has been assessed. In order to do so, an analysis based on the finite element method and dislocation density model is utilized, and microhardness measurement is carried out to verify the trends of analysis results. By comparing FEM results with experimental data, the optimized geometrical parameters controlling the deformation behavior of the tube in tube channel pressing are determined to obtain the best strain homogeneity and minimum dimensional changes in tube  

The evolution of microstructure and the mechanical properties of an aluminum 6061 alloy tube subjected to a novel severe plastic deformation process called tube channel pressing were studied. Results show that the tube channel pressing causes an impressive grain refinement and strengthening of the material. As an illustration, mostly ultrafine grained tube (D-=760nm) bearing the yield strength of 352. MPa can be obtained after 5 passes of tube channel pressing. Additionally, the tube channel pressing causes the heterogeneous grain refinement resulting in a bimodal distribution of size of grains after 7th pass. Therefore, it can be inferred that the main microstructure refining mechanism... 

In this work, the 6061 aluminum alloy tubes are severely deformed through a novel method called Tube Channel Pressing (TCP). The ability of this process in improving mechanical properties, grain refinement and microstructural changes of the alloy with different heat treatments before and after TCP process is investigated. Results show that TCP has notable effect on grain refinement and decreases crystallite size of solid solution treated aluminum 6061 material to 52. nm after equivalent strain of 3.09 which is comparable with the measured data from other SPD processes. The strength of the specimens aged before TCP is higher than that of those aged after TCP. The specimens artificially aged... 

Natural aging behavior of the aluminum 6061 alloy after a novel Severe Plastic Deformation process called Tube Channel Pressing (TCP) was studied. For this purpose, Vickers microhardness test was used to investigate the changes of mechanical properties while TEM and XRD observations were utilized in order to characterize microstructural evolution during natural aging. Results show that Si-enriched precipitates appear and coarsen rapidly in the first few days of natural aging of TCPed aluminum 6061 alloy which causes consecutive increase and decrease of Vickers microhardness, respectively. Similarly, other alloying elements such as Cu and Fe lead to formation of coarse precipitates during... 

This study is aimed to realize evolution of microstructure and mechanical properties of aluminum 6061 alloy tube subjected to Severe Plastic Deformation (SPD) and subsequent annealing. For this purpose, the tube is initially processed by different passes of an SPD process called Tube Channel Pressing (TCP) and then subjected to a subsequent annealing at 473. °K for 2. h. Afterwards, tension test is used for the evaluation of mechanical properties while Electron Back-Scattered Diffraction (EBSD) equipped Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM) are utilized for the microstructural characterizations. Results show that the Continuous Static Recrystallization... 

Nanowire arrays of copper oxide were first grown vertically using simple and cost effective thermal oxidation method on a copper foil. Subsequently, in order to deposit and grow PbS nanocyrstalline thin films on CuO NWs by utilizing the chemical bath deposition technique, these arrays were immersed as the substrate in the reaction solution consisting of Pb(NO3)2, (NH2)2CS and NaOH. The final products were characterized in detail by which the formation of uniform, unique arrays of CuO@PbS core–shell NWs was confirmed. Due to the nature of methods employed in synthesis of this hetero structure, the tuning of core and shell size and consequently properties of the novel structure is easily...